Data sheet:
Uncured Properties |
||
黏著劑類別 |
樹脂 |
|
類型 |
UV 曝光 |
|
曝光能量 (mJ/cm2) |
2000 |
|
UV燈波長 (nm) |
200~420 |
|
適當物質 |
Glass-Glass |
|
外觀 |
透明無色 |
|
黏度(cps) |
1800±200 |
Brookfield LVT Viscometer (Spindle #4, 60rpm, 25 °C) |
比重(g/cm3) |
1.086 |
Density meter |
折射率(before cure) |
1.4964 |
Abbe @ 25 °C |
Cured Properties |
||
硬度(type E) |
17(3000); 18(6000,10000) |
JIS K 6253-2006 |
折射率 |
1.5042 |
Abbe @ 25 °C |
比重(g/cm3) |
1.115 |
Density meter |
收縮率 (%) |
2.6 |
Density meter |
吸水度(%) |
0.27 |
JIS K7136 |
透明度(%) |
98.9 |
JIS K7136 |
L* |
96.46 |
|
a* |
-0.34 |
|
b* |
0.35 |
|
Reliability (Glass to glass) |
Pass* |
60 °C/90 % RH for 500 hrs 85 °C for 500 hrs -35 °C for 500 hrs -35 °C - 80 °C 100 cycles Dwell time: 30 mins |
儲藏時間 |
12 個月 |
|
保存條件 |
25 ± 5 °C |
*Two 0.5mm soda lime glasses were bonded together with 0.1-0.2mm . After visual inspection, no appreciable deterioration appears in visible appearance and physical integrity.